Poly lactic acid resin, also PLA resin or Polylactide resin, which is a 100% biodegradable resin. This Poly lactic acid resin is polymerized from lactic acid derived from plant sources such as corn.
Item No.:
All seriesBrand:
iSuoChem or OEMColor:
whiteAppearance:
granulesMOQ:
1000kgsFeatures:
100% biodegradable
Physical Property
|
Poly lactic acid resin |
P180 |
P180S |
P360 |
P380 |
P380S |
M580 |
Test Standard |
|
Density (g/cm3) |
1.24 |
1.28 |
1.24 |
1.35±0.05 |
1.35±0.05 |
1.26 |
GB/T 1033-2008 |
|
Melting Index (g/10min) 190℃, 2.16kg |
3-6 |
3-5 |
15±5 |
15±5 |
15±5 |
3-5 |
GB/T 3682-2000 |
|
Melting Point(℃) |
178±3 |
\ |
165±3 |
178±3 |
178±3 |
\ |
GB/T 19466.3-2004 |
|
GT Temperature(℃) |
61±2 |
\ |
61±2 |
\ |
61±2 |
\ |
GB/T 19466.2-2004 |
Mechanical Property
|
Poly lactic acid resin |
P180 |
P180S |
P360 |
P380 |
P380S |
M580 |
Test Standard |
|
Tensile strength(MPa)
|
≥55 |
≥25 |
≥50 |
≥45 |
≥45 |
≥25 |
GB/T 1040-2006 |
|
Impact strength(KJ/m2) Izod |
≥3 |
\ |
≥3 |
≥3 |
≥8 |
\ |
GB/T 1043-2008 |
|
Elongation at Break(%) |
≥3 |
≥80 |
≥5 |
≥5 |
≥20 |
≥100 |
GB/T 1040-2006 |
|
Heat Resistant(℃) HDT (amorphous) HDT(crystallize) |
55-60
100-110
|
55-60 |
\ |
55-60
100-110
|
55-60
100-110
|
55-60 |
\ |
APPLICATION 
P180
P180S
P360
P380
P380S
M580
Suggested
Application
Extrusion
(3D printing/ spinning)
Extrusion
(Straw)
Transparent injection
(Cold drinking cup)
Heat resistant injection
(Disposable items)
Heat resistant injection
(Durable goods)
Extrusion
(Blowing film)
WHY CHOOSE US
Professional technical team: senior PLA resin experts leading Asia in bio-based material technology.
Professional R&D team: specialized in the accurate development of bio-based material and products.
Professional after-sales team: able to solve any problems in the use of bio-based materials for over 10 years.
MATERIAL FEATURE
This is suit for various processing method. The heat resistance of products will increase to over 100℃after annealing.
More environmentally: 100% degradable and compostable in industrial compost processing.
More use: different series for extrusion, injection molding, spinning fiber, film or 3D printing.
MARKET ADVANTAGE
PLA lactic acid resin is a degradable material which is eligible to the development direction of global market and policy.
High acceptance: a acknowledged environmental-friendly material conform to different countries or regions.
High security: free from plasticizer, BPA of heavy metals.
High growth: hot in global market with a over 100% annual increase.